WAM® 90 ULC – Ultra Low Cement Castable

WAM® 90 ULC is a very high temperature, ultra-low cement containing castable comprised primarily of a pure tabular alumina aggregate. The alumina content, purity and lower cement levels in this product permit usage up to 3300oF.

 

Tabular alumina is a very high temperature aggregate with a very high melting point that is susceptible to creep (a tendency to deform at high temperatures under load). WAM® 90 ULC however, contains an appropriate amount of reactive silica which forms mullite at high temperatures and counteracts creep. This allows WAM® 90 ULC to be used as lintels and other load bearing applications. WAM® 90 ULC is also excels in high temperature chemically reactive conditions.

 

Westmoreland Advanced Material LLC’s  ultra-low cement castable technology incorporates the latest available technology in regards to particle size distribution, surfactants, and in-situ reactants that promote volume stability at temperature, density, non-reactivity, water demand, working time and placement characteristics. You will not find a superior product in the market place.

 

Several versions of these ultra-low cement castables are available including a coarse mix that  increases the material’s resistance to both abrasion and impact. Also available are add on packages for aluminum penetration resistance, alkali resistance, and thermal shock resistance. A fine package is available for patching and  intricate precast shapes.

 

WAM® 90 ULC finds application in several areas as a very high temperature, thermal protection material also required to resist chemical reaction. It is commonly used in controlled atmosphere reaction furnaces, specifically in reducing atmospheres.

Typical Technical Data
WAM® 90 ULC                                                                                        PDF Download

Classification:Ultra Low Cement Castable
Placement Method:Vibration Casting
Available Application Packages:AL - Aluminum Penetration Resistant
C - Coarse Aggregate
F - Fine Aggregate
TSR - Thermal Shock Resistant
Typical Water Requirement (%wt):4.5
Material Required for Estimating (lb/ft3):185
Maximum Recommended Service Temperature (°F):3300

CHEMICAL ANALYSIS
Calculated wt.% Based on Common Oxides

Aluminum Oxide (Al2O3):89.7 %
Silicon Dioxide (SiO2):8.9 %
Titanium Dioxide (TiO2):<0.1 %
Iron(III) Oxide (Fe2O3):0.1 %
Calcium Oxide (CaO):1.0 %
Magnesium Oxide (MgO):<0.1 %
Combined Alkali Oxide (Na2O + K2O):0.3 %

PHYSICAL PROPERTIES

Temperature
(°F)
Density
(lb/ft3)
Modulus of
Rupture (psi)
Cold Crushing
Strength (psi)
Permanent
Linear Change (%)
After 23018915308730n/a
After 150018516508920-0.1
After 3000n/an/an/a-0.2

Additional technical data may be available. Please contact your sales representative for more information.
Data on this table represent typical properties and cannot be used for specification purposes.