WAM® 80 RG – Reduced Cement Gunning Mix

WAM® 80 RG is a high duty reduced cement gunning mix.

WAM® gun mixes are mineralogically identical to their castable counterparts. WAM® 80 RG utilizes a bauxite containing aggregate system and is thus used in high abrasion applications. These gunning mixes are designed to optimize the gunning characteristics of the material. This results in a slightly smaller average particle size. These gunning mixes are manufactured with a proprietary technology which drastically reduces the amount of rebounds and results in a material that is easy to gun.

 

WAM® reduced cement gunning mix application areas are also identical to their castable counterparts as a repair material used to maintain an increase the lifetime of the refractory lining. They are also very capable as original working linings when reduced installation time is desired or required.  Premium grade gunning mixes are used when reduced reactivity with the melt/slag is required or improved high temperature properties are desired. Reduced cement gunning mixes tend to be less reactive at high temperatures compared to their standard cement counterparts. However this is a generalization and you should check with your technical sales representative if you are unsure or have questions.

Typical Technical Data
WAM® 80 RG                                                                                           
PDF Download

Classification:Reduced Cement Gun Mix
Placement Method:Gunning
Available Application Packages:

AL - Aluminum Penetration Resistant
TSR - Thermal Shock Resistant

Pre-Dampening Water (%wt):0-5
Material Required for Estimating (lb/ft3):155
Maximum Recommended Service Temperature (°F):3000

CHEMICAL ANALYSIS
Calculated wt.% Based on Common Oxides

Aluminum Oxide (Al2O3):80.6 %
Silicon Dioxide (SiO2):12.3 %
Titanium Dioxide (TiO2):2.6 %
Iron(III) Oxide (Fe2O3):1.0 %
Calcium Oxide (CaO):3.1 %
Magnesium Oxide (MgO):0.1 %
Combined Alkali Oxide (Na2O + K2O):0.3 %

PHYSICAL PROPERTIES

Temperature
(°F)
Density
(lb/ft3)
Modulus of
Rupture (psi)
Cold Crushing
Strength (psi)
Permanent
Linear Change (%)
After 230160218010,980n/a
After 150015514409,230-0.1
After 2500n/an/an/a+1.0

Additional technical data may be available. Please contact your sales representative for more information.
Data on this table represent typical properties and cannot be used for specification purposes.