WAM® 60 LC – Alumina Based Low Cement Castable

WAM® 60 LC is a high temperature, low cement, castable comprised primarily of a 60% alumina mullite containing aggregate. The amount of mullite contained in this aggregate is significantly more than the lower alumina containing aggregate present in the WAM® 50 LC. As a result of the increased mullite content and lower cement levels in this product, it is suitable for use up to 3,000oF.

 

Westmoreland Advanced Materials, LLC low cement castable compositions incorporate the latest available technology in regards to particle size distribution, surfactants, and in-situ reactants that promote volume stability at temperature, density, non-reactivity, water demand, working time and placement characteristics. You will not find a superior product in the market place. It is available in several versions. You will not find a superior product in the market place. It is available in several versions. The coarse version increases the material abrasion and impact resistance. Packages are made available for aluminum penetration resistance, alkali resistance, and thermal shock resistance. A fine package is also available for patching and  intricate precast shapes.

 

WAM® 60 LC finds application in several areas as a high temperature, low reactivity thermal protection material. This includes furnaces, ladles, and other furniture  for iron and steel foundries and mills, kiln car decks, annealing furnaces and bases, soaking pits, ladle lip rings, The AL version has been used in all aluminum processing and transport vessels and has been used in a variety of rotary kiln and hearth furnace applications as well. The TSR version has been used to cast burner blocks.

Typical Technical Data
WAM® 60 LC                                                                                            PDF Download

Classification:Low Cement Castable
Placement Method:Vibration Casting, Pumping / Shotcreteing
Available Application Packages:AL - Aluminum Penetration Resistant
C - Coarse Aggregate
F - Fine Aggregate
AR - Alkali Resistant
TSR - Thermal Shock Resistant
Typical Water Requirement (%wt):5
Material Required for Estimating (lb/ft3):158
Maximum Recommended Service Temperature (°F):3000

CHEMICAL ANALYSIS
Calculated wt.% Based on Common Oxides

Aluminum Oxide (Al2O3):61.5 %
Silicon Dioxide (SiO2):33.2 %
Titanium Dioxide (TiO2):1.9 %
Iron(III) Oxide (Fe2O3):0.9 %
Calcium Oxide (CaO):2.2 %
Magnesium Oxide (MgO):0.1%
Combined Alkali Oxide (Na2O + K2O):0.2 %

PHYSICAL PROPERTIES

Temperature
(°F)
Density
(lb/ft3)
Modulus of
Rupture (psi)
Cold Crushing
Strength (psi)
Permanent
Linear Change (%)
After 230160284024,920n/a
After 1500158239016,700-0.3
After 3000n/an/an/a+0.8

Additional technical data may be available. Please contact your sales representative for more information.
Data on this table represent typical properties and cannot be used for specification purposes.