WAM® 60 EMT – Enhanced Matrix Technology

WAM® 60 EMT is a general purpose enhanced monolithic castable.  It has the properties of a low cement castable with the robustness of a standard cement castable. It is composed primarily of a mullite containing aggregate. This allows the material to be suitable for use up to 2900oF.


Similar to standard cement castables, EMT castables are very forgiving and are less susceptible to temperature variations relative to set and working times and are very easy to place with typical vibration methods. However, like a low cement castable they require less water which results in better physical properties. In addition, unlike a standard cement castable, EMT castables can be pumped and shotcreted.


WAM® 60 EMT finds application in several areas as a high temperature, low reactivity thermal protection material. This includes furnaces, ladles, and other furniture  for iron foundries and mills, kiln car decks, annealing furnaces and bases, soaking pits, ladle lip rings.  It has been used in a variety of rotary kiln and hearth furnace applications as well. The TSR version has been used to cast burner blocks and is a very popular material for burner blocks used in aluminum furnaces.

Typical Technical Data
WAM® 60 EMT                                                                                        
PDF Download

Classification:Enhanced Monolithic Castable
Placement Method:Vibration Casting, Pumping / Shotcreteing
Available Application Packages:AL - Aluminum Penetration Resistant
C - Coarse Aggregate
F - Fine Aggregate
AR - Alkali Resistant
TSR - Thermal Shock Resistant
Typical Water Requirement (%wt):7
Material Required for Estimating (lb/ft3):152
Maximum Recommended Service Temperature (°F):2900

Calculated wt.% Based on Common Oxides

Aluminum Oxide (Al2O3):59.4 %
Silicon Dioxide (SiO2):31.3 %
Titanium Dioxide (TiO2):2.5 %
Iron(III) Oxide (Fe2O3):1.1 %
Calcium Oxide (CaO):5.3 %
Magnesium Oxide (MgO):0.2 %
Combined Alkali Oxide (Na2O + K2O):0.2 %


Modulus of
Rupture (psi)
Cold Crushing
Strength (psi)
Linear Change (%)
After 23015816308770n/a
After 150015210007500-0.1
After 2800n/an/an/a+0.2

Additional technical data may be available. Please contact your sales representative for more information.
Data on this table represent typical properties and cannot be used for specification purposes.