WAM® 45 CG G – Construction Grade Standard Cement Gun Mix

WAM® 45 CG G is a general purpose standard cement containing gunning mix.  Like their premium counterparts WAM® CG gun mixes are mineralogically identical to their castable counterparts. WAM® 45 CG G utilizes a fire clay based aggregate system.

 

These gunning mixes are designed to optimize the gunning characteristics of the material. This results in a slightly smaller average particle size. These gunning mixes are manufactured with a proprietary technology which drastically reduces the amount of reboundsand results in a material that is easy to gun.

 

WAM® CG gunning mix application areas are also identical to their economical castable counterparts as a repair material used to maintain an increase the lifetime of the refractory lining. They are also very capable as original working linings when reduced installation time is desired or required.

Typical Technical Data
WAM® 45 CG G                                                                                        PDF Download

Classification:Standard Cement Gun Mix
Placement Method:Gunning
Available Application Packages:

AL - Aluminum Penetration Resistant
TSR - Thermal Shock Resistant

Pre-Dampening Water (%wt):0-5
Material Required for Estimating (lb/ft3):118
Maximum Recommended Service Temperature (°F):2600

CHEMICAL ANALYSIS
Calculated wt.% Based on Common Oxides

Aluminum Oxide (Al2O3):40.4 %
Silicon Dioxide (SiO2):

48.5 %

Titanium Dioxide (TiO2):

1.9 %

Iron(III) Oxide (Fe2O3):

1.5 %

Calcium Oxide (CaO):

5.9 %

Magnesium Oxide (MgO):

0.4 %

Combined Alkali Oxide (Na2O + K2O):

1.4 %

PHYSICAL PROPERTIES

Temperature
(°F)
Density
(lb/ft3)
Modulus of
Rupture (psi)
Cold Crushing
Strength (psi)
Permanent
Linear Change (%)
After 230

126

840

3940

n/a
After 1500

118

580

3150

-0.2

After 2500n/an/an/a

+0.3

Additional technical data may be available. Please contact your sales representative for more information.
Data on this table represent typical properties and cannot be used for specification purposes.